Purchase your copy of ASTM C – 88() as a PDF download or hard copy directly from the official BSI Shop. All BSI British Standards. Designation: C − 88 (Reapproved ) Standard Test Method for For referenced ASTM standards, visit the ASTM website, , or. Find the most up-to-date version of ASTM C at Engineering

Author: Dalkree Tojas
Country: Romania
Language: English (Spanish)
Genre: Technology
Published (Last): 8 August 2018
Pages: 307
PDF File Size: 5.69 Mb
ePub File Size: 6.71 Mb
ISBN: 727-2-16802-770-8
Downloads: 44032
Price: Free* [*Free Regsitration Required]
Uploader: Goltilrajas

ASTM C 773 – 88

Ideally, ceramics should be stressed this way in use. NOTE 1—It is desirable to include details of the origin of the specimen and subsequent treatment.

Enviado por F773 flag Denunciar.

Originally published as C — 74 to replace C and C They may be formed and matured for the purpose of compression testing, or they may be cut from matured whitew- are by sawing or coredrilling. C 5 compressive strength of the specimen, psi or MPa; P 5 total load on the specimen at failure, lbf or N; and A 5 calculated area of the bearing surface of the specimen, in. The spherical surfaces shall be well lubricated, and the center of curvature shall lie on the lower face of the platen.

  DISCRASIAS CELULAS PLASMATICAS PDF

ASTM International – Laboratory Directory – University of Dayton Research Institute

The ends of c773 specimens shall be ground or lapped to yield plane and parallel faces. New cushion pads shall be used for each specimen. A number in parentheses indicates the year of last reapproval. Current edition approved Sept. Precision and Bias 8.

ASTM C773 – 88(2016)

This test is a measure of the potential load-bearing usefulness of a ceramic. One operator in each laboratory tested ten specimens of each material. C — 88 Reapproved Standard Test Method for Compressive Crushing Strength of Fired Whiteware Materials1 This standard is issued under the fixed designation C ; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision.

If the contact block is cracked during testing, it shall be replaced. Place an appropriate guard around the specimen to contain flying fragments at failure; eye protection should be used by the operator.

  ANUARUL STATISTIC AL ROMANIEI 2008 PDF

Single-operator component Between-laboratory component 1. Discard any pieces exhibiting cracks or flaws visible to the unaided eye. Significance and Use 3.

These faces shall be perpendicular. Suitable materials for cushion pads, selected in accordance with the compressive strength range of the material being tested, are shown in the following table: A superscript epsilon e indicates an editorial change since the last revision or reapproval.

The compo- nents of variance for compressive strength results expressed as coefficients of variation were calculated as follows: Last previous edition C — 88 It is the responsibility of the user of this standard to establish appro- priate safety and health practices and determine the applica- bility of regulatory limitations prior to use.